摘要
The subject of this study is the oxidation of fuel rod cladding made of material Zr1Nb(0.1% O) in steam at temperatures in the range of 660℃ to 1200℃ with a surface in the initial state (after manufacturing - grinding) and after additional chemical etching. The changes in the microstructure of tubes due to the interaction with steam were investigated. A comparison was made between the oxidation rate of this material (weight gain) and the data on the oxidation of other alloys for nuclear power plants. The oxidation rate of Zr1Nb(0.1% O) is close to the oxidation rate of other zirconium alloys. It is shown that after chemical treatment of the surface of the samples there is a more even growth of oxide films, and they have a smaller thickness for the same time of exposure than after mechanical grinding. Surface treatment before oxidation also affects the change of microstructure of samples when heated to high temperatures.