摘要
A combined model to predict austenite grains growth of titanium micro-alloyed as-cast steel during reheating process was established.The model invoIves the behaviors of austenite grains growth in continuous heating process and isothermal soaking process,and the variation of boundary pinning efficiency caused by the dissolution and coarsening kinetics of sec on d-phase particles was also con sidered into the model.Furthermore,the experimental verificatio ns were performed to examine the prediction power of the model.The results revealed that the mean austenite grains size increased with the increase in reheating temperature and soaking time,and the coarsening temperature of austenite grains growth was 1423 K under the current titanium content.In addition,the reliability of the predicted results in continuous heating process was validated by continuous heating experimenls.Moreover,an optimal regression expression of austenite grains growth in isothermal soaking process was obtained based on the experimental results.The compared results indicated that the combined model in conjunction with precipitates dissolution and coarsening kinetics had good reliability and accuracy to predict the austenite grains growth of titanium micro-alloyed casting steel during reheating process.
基金
National Natural Science Foundation of China(Grant Nos.51504048,51874060,51874059 and 51611130062)
The authors would like to acknowledge the members of Laboratory of Metallurgy and Materials,Chongqing University,for the support of this work.