摘要
工业生产大量排放SO2,使混凝土发生硫化发应,对混凝土结构的耐久性造成了严重影响。国内外混凝土中性化研究多集中于一般大气环境下的混凝土碳化问题,混凝土硫化研究较少。总结了近年来有关混凝土硫化问题的研究现状,从硫化机理出发,分析了硫化后混凝土的性能劣化规律,探讨了混凝土硫化速率的影响因素,并讨论了当前有关混凝土硫化研究的一些重要问题。
A large amount of SO 2 gas from industrial production reacts with concrete,which has a serious influence on durabi-lity of concrete structure.The domestic and foreign researches of concrete neutralization mainly focus on the concrete carbonation in general atmospheric environment;nevertheless,scant studies concern concrete sulfuration.This paper summarizes the research of concrete sulfuration in recent years,and reveals the mechanism of concrete sulfuration.The concrete deteriorated properties suffered sulfuration are analysed,and the influence factors of concrete sulfuration are considered.Finally,some important issues of are discussed.
作者
牛荻涛
吕瑶
刘西光
NIU Ditao;LU Yao;LIU Xiguang(School of Civil Engineering,Xi’an University of Architecture and Technology,Xi’an 710055)
出处
《材料导报》
EI
CAS
CSCD
北大核心
2017年第23期163-170,共8页
Materials Reports
基金
国家重点研发计划(2016YFC0701304)
教育部"创新团队发展计划"(IRT_17R84)
中国博士后科学基金(2016M602940XB)
西安建筑科技大学优秀博士论文培育基金
关键词
二氧化硫
混凝土
硫化机理
劣化规律
sulfur dioxide
concrete
sulfated mechanism
deterioration