A sample of sulfated anatase TiO2 with high‐energy(001)facets(TiO2‐001)was prepared by a simple one‐step hydrothermal route using SO42-as a morphology‐controlling agent.After doping ceria,Ce/TiO2‐001 was used as the catalyst for selective catalytic reduction(SCR)of NO with NH3.Compared with Ce/P25(Degussa P25 TiO2)and Ce/P25‐S(sulfated P25)catalysts,Ce/TiO2‐001 was more suitable for medium‐and high‐temperature SCR of NO due to the high surface area,sulfation,and the excellent properties of the active‐energy(001)facets.All of these facilitated the generation of abundant acidity,chemisorbed oxygen,and activated NOx‐adsorption species,which were the important factors for the SCR reaction.
氮氧化物(NO_x)是当今大气环境中的主要污染物之一,氨法选择性催化脱硝技术(NH_3-SCR)是最有前景的烟气脱硝技术之一.在众多的NH_3-SCR催化剂中,钛基催化剂由于其较好的热稳定性、抗硫性和环境友好性成为近年来研究的热点.本文以SO_4^(2-).离子作为晶面导向剂,采用一步水热法合成了具有(001)高能晶面的SO_4^(2-).-TiO_2,负载氧化铈后用于SCR反应,并以Ce/P25和Ce/P25-S(浸渍法硫酸化)作为参照对比.研究发现,Ce/TiO_2-001更适合于中、高温NH_3-SCR反应,在290 oC时NO转化率已达99%,并且在290–480 oC范围内均保持99%的脱硝效率.利用X射线衍射、N2吸附脱附、透射电子显微镜、X射线光电子能谱(XPS)、NH3/O2程序升温脱附(TPD)、傅里叶原位红外光谱等技术研究了上述催化剂的表面物化性质与脱硝性能的关系.相比于Ce/P25和Ce/P25-S,Ce/TiO_2-001具有更高的比表面积(107 m^2/g),形成了介孔TiO_2单晶,且晶粒尺寸更小.XPS和NH3-TPD结果表明,Ce/TiO_2-001表面具有丰富的酸性位.硫酸化可以增加催化剂表面的Brosted/Lewis酸性位;同时,(001)高能晶面有利于水分子的解离,从而促进酸性位的产生.O_2-TPD表明,Ce/TiO_2-001催化剂表面存在大量化学吸附氧,这与其一步合成中的硫酸化和(001)高能晶面密切相关,而化学吸附氧在中高温SCR反应中起着重要的作用.通过原位红外分析可得,不同催化剂表面所形成的NO_x吸附物种有所差异,在30°C时,Ce/P25的NO_x吸附物种比较丰富,存在气相NO2、双齿硝酸盐、线性硝酸盐、单齿硝酸盐和桥式硝酸盐,而Ce/P25-S和Ce/TiO_2-001上的NO_x吸附物种则以单齿硝酸盐/亚硝酸盐为主.随着温度的升高,以上催化剂表面的NO_x吸附物种逐渐变为以气相NO2和双齿硝酸盐为主.但同种NO_x吸附物种(气相NO2、双齿硝酸盐)在不同催化剂上的反应活性也有所不同,在250°C时,其顺序为:Ce/TiO_2-001>Ce/P25-S>Ce/P25,与脱硝性能相�
基金
supported by the National Key R&D Program of China(2016YFC0204100)
the Zhejiang Provincial "151" Talents Program
the Program for Zhejiang Leading Team of S&T Innovation(2013TD07)
the Changjiang Scholar Incentive Program(2009)~~