摘要
In this study we report a series of nickel-rich layered cathodes LiNi1-2xCoxMnxO2（x = 0.075, 0.05,0.025） prepared from chlorides solution via ultrasonic spray pyrolysis. SEM images illustrate that the samples are submicron-sized particles and the particle sizes increase with the increase of Ni content.LiNi0.85Co0.075Mn0.075O2 delivers a discharge capacity of 174.9 mAh g-1 with holding 93% reversible capacity at 1 C after 80 cycles, and can maintain a discharge capacity of 175.3 mAh g-1 at 5 C rate. With increasing Ni content, the initial specific capacity increases while the cycling and rate performance degrades in some extent. These satisfying results demonstrate that spray pyrolysis is a powerful and efficient synthesis technology for producing Ni-rich layered cathode（Ni content 〉 80%）.
In this study we report a series of nickel-rich layered cathodes LiNi1-2xCoxMnxO2（x = 0.075, 0.05,0.025） prepared from chlorides solution via ultrasonic spray pyrolysis. SEM images illustrate that the samples are submicron-sized particles and the particle sizes increase with the increase of Ni content.LiNi0.85Co0.075Mn0.075O2 delivers a discharge capacity of 174.9 mAh g-1 with holding 93% reversible capacity at 1 C after 80 cycles, and can maintain a discharge capacity of 175.3 mAh g-1 at 5 C rate. With increasing Ni content, the initial specific capacity increases while the cycling and rate performance degrades in some extent. These satisfying results demonstrate that spray pyrolysis is a powerful and efficient synthesis technology for producing Ni-rich layered cathode（Ni content 〉 80%）.
基金
financial support of the National Basic Research Program of China (2014CB643406)
the National Natural Science Foundation of China (51674296, 51704332)
the National Postdoctoral Program for Innovative Talents (BX201700290)
the Fundamental Research Funds for the Central Universities of Central South University (2017zzts125)