摘要
The microwave absorbents of Fe and C nanoparticles as magnetic loss and dielectric loss material respectively were composited with the polyvinyl alcohol （PVA） as binder by spray granulation method, The electromagnetic parameters of Fe and C composite particles were analyzed by vector network. The complex permittivity and magnetic permeability of Fe and C composite particles matched well with increasing C nanoparticle content, and then the microwave loss property was improved. A minimum reflection loss （RL） of -42.7 dB at 3.68 GHz for a composite with 4.6 mm in thickness can be obtained when the content ratio of the C nanoparticles, the modified Fe nanoparticles and the PVA is 21：49：30 （Sample 3）.
The microwave absorbents of Fe and C nanoparticles as magnetic loss and dielectric loss material respectively were composited with the polyvinyl alcohol （PVA） as binder by spray granulation method, The electromagnetic parameters of Fe and C composite particles were analyzed by vector network. The complex permittivity and magnetic permeability of Fe and C composite particles matched well with increasing C nanoparticle content, and then the microwave loss property was improved. A minimum reflection loss （RL） of -42.7 dB at 3.68 GHz for a composite with 4.6 mm in thickness can be obtained when the content ratio of the C nanoparticles, the modified Fe nanoparticles and the PVA is 21：49：30 （Sample 3）.
基金
the support from the National Natural Science Foundation of China(No.51171033)
the Fundamental Research Funds for the Central Universities(DUT15LAB05,DUT16LAB03)