摘要
A series of SBA-15-supported chromia-ceria catalysts with 3% Cr and 1%--5% Ce （3Cr-Ce/SBA） were pre- pared using an incipient wetness impregnation method. The catalysts were characterized by XRD, N2 adsorption, SEM, TEM-EDX, Raman spectroscopy, UV-vis spectroscopy, XPS and H2-TPR, and their catalytic performance for isobutane dehydrogenation with CO2 was tested. The addition of ceria to SBA-15-supported chromia improves the dispersion of chromium species. 3Cr-Ce/SBA catalysts are more active than SBA-15-supported chromia （3Cr/SBA）, which is due to a higher concentration of Cr^6＋ species present on the former catalysts. The 3Cr-3Ce/SBA catalyst shows the highest activity, which gives 35.4% isobutane conversion and 89.6% isobutene selectivity at 570℃ after 10 min of the reaction.
A series of SBA-15-supported chromia-ceria catalysts with 3% Cr and 1%--5% Ce （3Cr-Ce/SBA） were pre- pared using an incipient wetness impregnation method. The catalysts were characterized by XRD, N2 adsorption, SEM, TEM-EDX, Raman spectroscopy, UV-vis spectroscopy, XPS and H2-TPR, and their catalytic performance for isobutane dehydrogenation with CO2 was tested. The addition of ceria to SBA-15-supported chromia improves the dispersion of chromium species. 3Cr-Ce/SBA catalysts are more active than SBA-15-supported chromia （3Cr/SBA）, which is due to a higher concentration of Cr^6＋ species present on the former catalysts. The 3Cr-3Ce/SBA catalyst shows the highest activity, which gives 35.4% isobutane conversion and 89.6% isobutene selectivity at 570℃ after 10 min of the reaction.