When aprotic Li-O2 batteries recharge, the solid Li2O2 in the positive electrode is oxidized, which often exhibits a continuous or step increase in the charging potential as a function of the charging capacity, and its origin remains incompletely understood. Here, we report a model study of electro-oxidation of a Li2O2 film on an Au electrode using voltammetry coupled with in situ Raman spectroscopy. It was found that the charging reaction initializes at the positive electrodelLizO2 interface, instead of the previously presumed Li2O2 surface, and consists of two temporally and spatially separated Li2O2 oxidation processes, accounting for the potential rise during charging of Li-O2 batteries. Moreover, the electrode surface-initialized oxidation can disintegrate the Li2O2 film resulting in a loss of Li2O2 into electrolyte solution, which drastically decreases the charging efficiency and highlights the importance of using soluble electro-catalyst for the complete charging of Li-02 batteries.
When aprotic Li-O_2 batteries recharge, the solid Li_2O_2 in the positive electrode is oxidized, which often exhibits a continuous or step increase in the charging potential as a function of the charging capacity, and its origin remains incompletely understood.Here, we report a model study of electro-oxidation of a Li_2O_2 film on an Au electrode using voltammetry coupled with in situ Raman spectroscopy. It was found that the charging reaction initializes at the positive electrode|Li_2O_2 interface, instead of the previously presumed Li_2O_2 surface, and consists of two temporally and spatially separated Li_2O_2 oxidation processes, accounting for the potential rise during charging of Li-O_2 batteries. Moreover, the electrode surface-initialized oxidation can disintegrate the Li_2O_2 film resulting in a loss of Li_2O_2 into electrolyte solution, which drastically decreases the charging efficiency and highlights the importance of using soluble electro-catalyst for the complete charging of Li-O_2 batteries.
基金
supported by the National Natural Science Foundation of China (91545129, 21575135, 21605136)
the “Strategic Priority Research Program” of the Chinese Academy of Science (XDA09010401)
the National Key Technology Research and Development Program of China (2016YBF0100100)
the Science and Technology Development Program of the Jilin Province (20150623002TC, 20160414034GH)