增材制造(AM)技术对成型复杂结构零件有显著优势,但以选区激光熔融技术为代表的金属增材制造技术固有的"粉末粘附"、"球化效应"所导致的毛糙表面,使零件难以满足使用要求。采用混合粒径磨料介质对增材制造铝合金格栅外表面及细小内孔进行一体化抛光试验研究。通过分析磨粒流加工过程各阶段的微观形貌和表面轮廓测量结果等来研究材料去除过程中零件表面形貌、材料去除和表面粗糙度变化。试验结果表明,磨粒流加工方法能够有效消除"球化效应"导致的零件表面的金属球团簇聚集现象,并能够对增材制造格栅零件外表面和内孔实现有效的抛光,格栅表面粗糙度从初始的14μm降至1.8μm。
Additive Manufacturing （AM） technology is obviously advantageous in producing parts with complex structures. However, it is difficult for the as-built surfaces of AM parts to meet the quality requirement, as the as-built surfaces are dete- riorated by the inherent characteristics of powder adhesion and bailing effect of metal AM technologies, e.g. Selective Laser Melting （SLM）. The Abrasive Flow Machining （AFM） is used to polish the outer and inner surfaces of additively manufac- tured aluminum grille parts, with the abrasive media containing grits of different sizes. The variations of surface topology, material removal and surface roughness of the grille are considered by analyses of measurements of micro-topology and pro- files during the AFM process. The experiment results show that clustering of molten metal balls due to the bailing effect can be removed effectively from the grille surface, and the surface roughness is reduced from the initial 14 μm to the final 1.8 μm, with pretty good polishing effect being achieved for the outer and inner surfaces of the grille.
作者
高航
李世宠
付有志
魏海波
彭灿
王宣平
GAO Hang LI Shichong FU Youzhi WEI Haibo PENG Can WANG Xuanping(Key Laboratory for Precision and Non-traditional Machining Technology of Ministry of Education, Dalian University of Technology, Dalian 116024, China)
出处
《航空学报》
EI
CAS
CSCD
北大核心
2017年第10期226-234,共9页
Acta Aeronautica et Astronautica Sinica
基金
国家自然科学基金创新群体"精密制造理论与技术基础研究"(51621064)
国家自然科学基金面上项目(51475074)
中央高校基本科研业务费专项资金(DUT15QY37)
装备预研教育部联合基金(6141A02022106)~~
关键词
增材制造(AM)
球化效应
粉末粘附
铝合金格栅
磨粒流加工
磨削
Additive Manufacturing （AM）
bailing effect
powder adhesion
aluminum alloy grille
abrasive flow machi-ning
abrasive machining