Leached Pt-Fe and Pt-Co catalysts were prepared by acid leaching the reduced catalysts in acid solution. Oxidation treatments of leached catalysts produced the structure o f metal oxides decorat-ing the surface of nanoparticles. The fully oxidized Fe2O3 and Co3O4 species on Pt nanoparticle sur-faces result in the low performance of the CO complete oxidation （COOX） reaction. In contrast, un-saturated FeO and CoO surface species can be formed during exposure to the CO preferential oxida-tion （CO-PROX） reaction with an excess of H2, leading to a high O2 activation ability and enhancing the CO-PROX activity. The FeOx surface structures can be transformed between these two states by varying the reactive gas environments, exhibiting oscillating activity in these two reactions. Con-versely, the CoO surface structure formed in the H2 -rich atmosphere is stable when exposed to the COOX reaction and exhibits similar activity in these two reactions. It is hoped that this work may assist in understanding the important role of surface oxides in real reactions.
负载型纳米催化剂表面结构与其催化性能之间关系的研究一直受到广泛关注.由于其结构复杂使得人们在研究催化剂构效关系时遇到了很多困难.近年来,大量研究发现反转催化剂在众多反应中表现出优越的催化性能.反转催化剂是将过渡金属氧化物负载于其它金属表面.和传统金属/氧化物催化剂相比,反转催化剂更能突出氧化物在催化反应中的重要作用.众多研究表明,在氧化物-金属界面处存在特殊的作用,这种作用可以改变氧化物的电子特性和化学性质,进而产生较高的催化性能.傅强等人创建了金属氧化物负载于Pt表面的反转催化体系,其表现出了高的低温CO氧化反应性能.在氧化物和Pt之间的界面限域效应可以稳定氧化物中配位不饱和的金属阳离子.这种配位不饱和的氧化物提供了活化O_2的活性位.目前,反转催化剂的研究主要集中在单晶模型体系中,在负载型催化剂中的研究还较少.我们以炭黑(CB)为载体,将还原后的Pt-Fe和Pt-Co催化剂经过酸洗制备了一种表面富Pt核为合金的结构.考察了酸洗后的Pt-Fe和Pt-Co催化剂经过不同温度氧化后的结构变化,并讨论了其结构与CO完全氧化反应(COOX)和CO选择氧化反应(CO-PROX)性能的关系.X射线粉末衍射(XRD),电感耦合等离子体发射光谱(ICP),透射电镜(TEM)和X射线光电子能谱(XPS)表征结果表明,还原后的Pt基催化剂经过酸洗可以选择性去除纳米粒子表面的3d过渡金属,形成表面富Pt体相为合金的结构.将酸洗后的Pt-Fe和Pt-Co催化剂在不同温度下空气中氧化,发现近表层的Fe(Co)会扩散到粒子表面上,形成过度氧化的Fe_2O_3(Co_3O_4)表面结构.氧化后的催化剂在COOX和CO-PROX反应中表现出截然不同的催化性能.酸洗后的Pt-Fe(Pt-Co)催化剂经过不同温度氧化后在COOX反应中活性都较差,室温下的CO转化率只有不到30%,CO完全转化的温度超过100 ℃,相当于纯Pt�
基金
supported by the National Natural Science Foundation of China(21403004,21403003)~~