摘要
Single-phase insulating 12CaO？7Al_2O_3（C12A7） powder was synthesized using an optimized hydrothermal method. Pure phase of C12A7 was got at a comparatively lower temperature（c.a. 300 ℃） than that has been previously reported. The crystallite size of the synthesized C12A7 powder was 7±2 nm. The surface area values calculated for all the samples at a synthesis temperature range of 250-800 ℃ for 5 h were in the range of about 19-24 m^2/g, with pore sizes of 12-20 nm. This low-temperature-based synthetic strategy along with nano porous structures and a high surface area value can facilitate catalyst application.
Single-phase insulating 12CaO？7Al_2O_3（C12A7） powder was synthesized using an optimized hydrothermal method. Pure phase of C12A7 was got at a comparatively lower temperature（c.a. 300 ℃） than that has been previously reported. The crystallite size of the synthesized C12A7 powder was 7±2 nm. The surface area values calculated for all the samples at a synthesis temperature range of 250-800 ℃ for 5 h were in the range of about 19-24 m^2/g, with pore sizes of 12-20 nm. This low-temperature-based synthetic strategy along with nano porous structures and a high surface area value can facilitate catalyst application.
基金
Funded by the National Natural Science Foundation of China(No.21377063)
the Zhejiang Natural Science Foundation(No.LY15F040004)
the Program for Ningbo Key Laboratory of Silicon and Organic Thin Film Optoelectronic Technologies