Isothermal hot compression tests of as-cast high-Cr ultra-super-critical（USC） rotor steel with columnar grains perpendicular to the compression direction were carried out in the temperature range from 950 to 1250°C at strain rates ranging from 0.001 to 1 s^（-1）. The softening mechanism was dynamic recovery（DRV） at 950°C and the strain rate of 1 s^（-1）, whereas it was dynamic recrystallization（DRX） under the other conditions. A modified constitutive equation based on the Arrhenius model with strain compensation reasonably predicted the flow stress under various deformation conditions, and the activation energy was calculated to be 643.92 kJ ×mol^（-1）. The critical stresses of dynamic recrystallization under different conditions were determined from the work-hardening rate（θ）–flow stress（σ） and-θ/σ–σ curves. The optimum processing parameters via analysis of the processing map and the softening mechanism were determined to be a deformation temperature range from 1100 to 1200°C and a strain-rate range from 0.001 to 0.08 s^（-1）, with a power dissipation efficiency η greater than 31%.
Isothermal hot compression tests of as-cast high-Cr ultra-super-critical（USC） rotor steel with columnar grains perpendicular to the compression direction were carried out in the temperature range from 950 to 1250°C at strain rates ranging from 0.001 to 1 s^（-1）. The softening mechanism was dynamic recovery（DRV） at 950°C and the strain rate of 1 s^（-1）, whereas it was dynamic recrystallization（DRX） under the other conditions. A modified constitutive equation based on the Arrhenius model with strain compensation reasonably predicted the flow stress under various deformation conditions, and the activation energy was calculated to be 643.92 kJ ×mol^（-1）. The critical stresses of dynamic recrystallization under different conditions were determined from the work-hardening rate（θ）–flow stress（σ） and-θ/σ–σ curves. The optimum processing parameters via analysis of the processing map and the softening mechanism were determined to be a deformation temperature range from 1100 to 1200°C and a strain-rate range from 0.001 to 0.08 s^（-1）, with a power dissipation efficiency η greater than 31%.
基金
supported by the Major State Basic Research Development Program of China (No.2011CB012900)
the National Natural Science Foundation of China (No.51374144)
the Shanghai Rising-Star Program (No.14QA1402300)