Zr and its alloys have excellent mechanical properties as new structural material,but in specific application environment,its corrosion resistance still needs to be further explored.In this work,double glow plasma surface alloying technique was used for copperizing on pure Zr surface.Besides,X-ray diffraction（XRD）,scanning electron microscope（SEM） and energy dispersion spectrum（EDS） were employed to characterize the samples.Furthermore,research was also conducted on the polarization curve of the samples in different solutions.Copperizing on surface can improve corrosion resistance of pure Zr in 3.5 % Na Cl and 0.5 moláL-1Na OH solutions.Especially in 0.5 moláL-1Na OH solution,the corrosion resistance can achieve significant improvement.However,copperizing has no influence on the improvement of corrosion resistance of pure Zr in 0.5 moláL-1H2SO4 solution.The results may provide new insight into way for improving the corrosion property of zirconium alloys.
Zr and its alloys have excellent mechanical properties as new structural material,but in specific application environment,its corrosion resistance still needs to be further explored.In this work,double glow plasma surface alloying technique was used for copperizing on pure Zr surface.Besides,X-ray diffraction（XRD）,scanning electron microscope（SEM） and energy dispersion spectrum（EDS） were employed to characterize the samples.Furthermore,research was also conducted on the polarization curve of the samples in different solutions.Copperizing on surface can improve corrosion resistance of pure Zr in 3.5 % Na Cl and 0.5 moláL-1Na OH solutions.Especially in 0.5 moláL-1Na OH solution,the corrosion resistance can achieve significant improvement.However,copperizing has no influence on the improvement of corrosion resistance of pure Zr in 0.5 moláL-1H2SO4 solution.The results may provide new insight into way for improving the corrosion property of zirconium alloys.
基金
financially supported by the National Basic Research Program of China (No.2013CB733000)
the National Natural Science Foundation of China (Nos.51271161,51271162 and 51434008)