摘要
The process of pressure leaching the converter vanadium slag with waste titanium dioxide without roasting was studied. Mineralogy analysis indicates that the con- verter vanadium slag contains mainly three mineral phases： magnetite, titanium magnetite, and silicate phase. Vana- dium is in combination with iron, titanium, manganese, aluminum, and silicon. The impacts of leaching tempera- ture, leaching time, stirring speed, liquid-to-solid ratio, and initial leaching agent concentration were investigated on the waste titanium dioxide leaching process. The results indi- cate that under the optimal conditions, the vanadium and the iron leaching rates are 96.85 % and 93.50 %, respectively, and the content of titanium is 12.6 % in the residue. The main mineral phases for the residues under the optimal operation conditions are quartz, ilmenite, anatase, and sili- cate phase, and the residues can be reused as the extraction of titanium raw materials for titanium dioxide production technology by the sulfate method.
The process of pressure leaching the converter vanadium slag with waste titanium dioxide without roasting was studied. Mineralogy analysis indicates that the con- verter vanadium slag contains mainly three mineral phases： magnetite, titanium magnetite, and silicate phase. Vana- dium is in combination with iron, titanium, manganese, aluminum, and silicon. The impacts of leaching tempera- ture, leaching time, stirring speed, liquid-to-solid ratio, and initial leaching agent concentration were investigated on the waste titanium dioxide leaching process. The results indi- cate that under the optimal conditions, the vanadium and the iron leaching rates are 96.85 % and 93.50 %, respectively, and the content of titanium is 12.6 % in the residue. The main mineral phases for the residues under the optimal operation conditions are quartz, ilmenite, anatase, and sili- cate phase, and the residues can be reused as the extraction of titanium raw materials for titanium dioxide production technology by the sulfate method.
基金
financially supported by the Chinese National Programs for High Technology Research and Development(Nos.2010AA03A405 and 2012AA062303)
the National Natural Science Foundation of China(Nos.U1202274,51004033,51204040,and 50974035)
the National Science and Technology Support Program(No.2012BAE01B02)
the Fundamental Research Funds for the Central Universities(No.N100302005)
the Doctoral Fund Project(No.20120042110011)