采用自由基聚合法制备了p H敏感水凝胶聚丙烯酸,研究了该水凝胶在不同p H溶液中的溶胀行为。结果表明,聚丙酸水凝胶在酸性溶液中溶胀率较低,在碱性溶液中溶胀率较大,具有明显的p H敏感性能。以该水凝胶为吸附剂,研究了其对染料罗丹明B的吸附性能。结果显示,在p H=2.0的酸性条件下,聚丙烯酸水凝胶对罗丹明B的吸附率较大,而在p H=7.0的中性溶液中对罗丹明B的吸附率较小,并且聚丙烯酸水凝胶具有较好的重复利用性能。
In this study,p H-responsive poly（acrylic acid）（PAA） hydrogel was prepared via free radical polymerization.The swelling behaviors of PAA in aqueous solution at different p H values were investigated.The results demonstrated that the swelling ratio of PAA in acidic solution was much lower than that of in basic solution.Using the PAA as adsorbent,the adsorptive performance of PAA for rhodamine B was also investigated.The results showed that the adsorption rate for rhodamine B at p H = 2.0 was much higher than at p H = 7.0.In addition,PAA hydrogel have a good recycle rate for adsorption of rhodamine B.