磷酸镁水泥(MPC)是一种凝结硬化快、早期强度高、黏结强度高、干燥收缩小、耐磨、抗冻、生物相容性好的新型胶凝材料,无论在民用、军事建筑还是生物骨修复材料上都有很好的应用前景,因此得到了广泛的关注。主要对MPC的制备、水化产物、机理以及在生物医学领域的应用研究现状进行了综述。
Magnesium phosphate cement （MPC） is a kind of novel cementing material with rapid condensation sclerosis, high early strength, high compressive strength and little dry shrinkage, good wear resistance, good frost resistance and good biocompatibility. It exhibits excellent mechanical performance as civilian and military buildings materials or biological bone repair materials. Thus the research of this materials received extensive attention. The preparaion, hydration mechanism of MPC, and application of biomedical are reviewed.