摘要
利用光还原的方法制备一系列不同银含量的改性介孔二氧化钛的颗粒。采用X射线粉末衍射(XRD)、透射电子显微镜(TEM)、紫外一可见漫反射谱(DRS)和X射线能谱仪(EDX)等技术手段对制备的样品进行了表征。结果表明,银纳米粒子被牢牢固定在二氧化钛表面,并在银和二氧化钛界面形成肖特基势垒用以提高电子–空穴的分离。而从紫外可见漫反射光谱中看出,银二氧化钛样品与未改性的二氧化钛样品相比显示出更高的红移。以亚甲基蓝(MB)为光降解模型,银改性二氧化钛表现出较高的活性。
A series of Ag-modified mesoporous titania（TiO_2） particles with various silver contents were prepared by photoreduction. The prepared Ag-TiO_2 samples were characterized by X-ray diffraction（XRD）, transmission electron microscope（TEM）, energy dispersive X-ray spectrometry（EDX） and UV-visible diffuse reflectance spectroscopic（DRS） techniques. The visible light photocatalytic property was demonstrated for photodegradation of methylene blue（MB） solution. The results showed that Ag nanoparticles were firmly immobilized on the TiO_2 surface, which improved electron-hole separation by forming the Schottky barrier at the Ag-TiO_2 interface. The diffusion of reflectance UV-Vis spectra were also served as an indication that the Ag-TiO_2 samples displayed higher red shifts in comparison with un-modified TiO_2 sample. Under visible light, the optimal photoactivity was obtained for the sample m-TiO_2-Ag-2.0wt%. The TiO_2-Ag catalyst is likely to be used again for a number of times without any additional treatment.
出处
《无机材料学报》
SCIE
EI
CAS
CSCD
北大核心
2016年第5期555-560,共6页
Journal of Inorganic Materials
基金
National Natural Science Foundation of China(51272107)
Natural Science Foundation of Jiangsu Province,China(BK2011024)
关键词
银纳米粒子
介孔二氧化钛
光催化
光致还原
silver nanoparticles
mesoporous titania
photodegraduation
photoreduction