摘要
通过X射线衍射、扫描电镜、金相组织分析和拉伸性能测试等方法,研究了Al对Mg-5Gd-3Y铸态合金组织和性能的影响。结果表明,Mg-5Gd-3Y铸态合金的组织由α-Mg基体和共晶相Mg5Gd和Mg24Y5组成。加入Al元素后,有新相Al2Gd、Al2Y析出,对合金的晶粒起到细化作用,有效提高了Mg-5Gd-3Y铸态合金的力学性能。
The effects of aluminum on the microstructure and mechanical properties of as-cast Mg-5Gd-3Y alloy were studied by using X-ray diffraction,scanning electron microscopy,metallurgical microscopy and tensile performance test.The results show that as-cast Mg-5Gd-3Yalloy consists ofα-Mg matrix and eutectic phases of Mg5 Gd and Mg24Y5.After adding Al element to Mg-5Gd-3Yalloy,there are new Al2 Gd and Al2 Y phases separating out to effectively refine alloy grains and improve its mechanical properties.
出处
《稀有金属与硬质合金》
CAS
CSCD
北大核心
2016年第1期56-59,共4页
Rare Metals and Cemented Carbides