The ductility of as-fabricated Ti-6AI-4V fails far short of the requirements for biomedical titanium alloy implants and the heat treatment remains the only applicable option for improvement of their mechanical properties. In the present study, the decomposition of as-fabricated martensite was investigated to provide a general understanding on the kinetics of its phase transformation. The decomposition of as- fabricated martensite was found to be slower than that of water-quenched martensite. It indicates that specific heat treatment strategy is needed to be explored for as.fabricated Ti-6AI-4V. Three strategies of heat treatment were proposed based on different phase transformation mechanisms and classified as subtransus treatment, supersolvus treatment and mixed treatment. These specific heat treatments were conducted on selective laser melted samples to investigate the evolutions of microstructure and mechanical properties. The subtransus treatment leaded to a basket-weave structure without changing the morphology of columnar prior β grains. The supersolvus treatment resulted in a lamellar structure and equiaxed β grains. The mixed treatment yielded a microstructure that combines both features of the subtransus treatment and supersolvus treatment. The subtransus treatment is found to be the best choice among these three strategies for as.fabricated Ti-6AI-4V to be used as biomedical implants.
The ductility of as-fabricated Ti-6AI-4V fails far short of the requirements for biomedical titanium alloy implants and the heat treatment remains the only applicable option for improvement of their mechanical properties. In the present study, the decomposition of as-fabricated martensite was investigated to provide a general understanding on the kinetics of its phase transformation. The decomposition of as- fabricated martensite was found to be slower than that of water-quenched martensite. It indicates that specific heat treatment strategy is needed to be explored for as.fabricated Ti-6AI-4V. Three strategies of heat treatment were proposed based on different phase transformation mechanisms and classified as subtransus treatment, supersolvus treatment and mixed treatment. These specific heat treatments were conducted on selective laser melted samples to investigate the evolutions of microstructure and mechanical properties. The subtransus treatment leaded to a basket-weave structure without changing the morphology of columnar prior β grains. The supersolvus treatment resulted in a lamellar structure and equiaxed β grains. The mixed treatment yielded a microstructure that combines both features of the subtransus treatment and supersolvus treatment. The subtransus treatment is found to be the best choice among these three strategies for as.fabricated Ti-6AI-4V to be used as biomedical implants.
基金
Acknowledgements The authors are grateful for the financial support from the National Natural Science Foundation of China （Grant Nos. 51361130032 and 51472139） and the Doctor Subject Foundation of the Ministry of Education of China （Grant No. 20120002130002）.