使用简单的水热法,以十二烷基硫酸钠(SDS)为表面活性剂合成纳米SnO2,并利用X射线衍射仪(XRD)和扫描电子显微镜(SEM)分别对样品结构、颗粒大小和形貌进行了表征.结果表明,所制备的SnO2为金红石型结构,其粒径为7nm左右,粒子尺寸比较均匀,比表面积较大.光降解甲基橙的实验表明,加入样品SnO2催化剂的甲基橙溶液降解率可达到76.16%,加催化剂后,有机物的降解程度得到了极大改善.
In this paper, a simple hydrothermal method was used to synthesize nano two tin oxide （SDS） as a surfactant, and the structure, particle size and morphology were characterized by X ray diffraction （XRD） and scanning electron microscopy （SEM）. The results showed that the prepared SnO2 was rutile structure, with a particle size of about 7 nm; the particle size was uni- form, and the surface area was larger. The experiment shows that the photocatalytic degradation of methyl orange, adding samples of SnO2 catalyst of methyl orange degradation rate can reach 76.16%. After the catalyst, the degradation degree of organic matter was greatly improved.
出处
《淮海工学院学报（自然科学版）》
CAS
2015年第3期54-56,共3页
Journal of Huaihai Institute of Technology:Natural Sciences Edition
关键词
SNO2
水热法制备
光催化
甲基橙
SnO2
hydrothermal synthesis
photocatalysis
methyl orange