摘要
By means of optical microscope （OM）, X-ray diffraction （XRD）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM） analyses, the microstructures of as-cast and heat-treated Mg--4Zn-IY （wt%） alloy containing quasi-crystal phase were studied. The microstructure of the as-cast alloy consists of a-Mg solid solution grains, intermetallic particles and eutectic phases （W-phase and 1-phase）, and huge grains with seri- ous dendritic segregation are clearly observed. After heat treatment, phase transformation and dissolution occur in the alloy and many phases remain. When the alloy was treated above 410 ~C, the eutectic phases transform into spherical shape as the I-phase turns to W-phase. After heat treatment for long time, the alloy is over burnt and the W-phase decomposes to Mg-Y binary phase.
By means of optical microscope （OM）, X-ray diffraction （XRD）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM） analyses, the microstructures of as-cast and heat-treated Mg--4Zn-IY （wt%） alloy containing quasi-crystal phase were studied. The microstructure of the as-cast alloy consists of a-Mg solid solution grains, intermetallic particles and eutectic phases （W-phase and 1-phase）, and huge grains with seri- ous dendritic segregation are clearly observed. After heat treatment, phase transformation and dissolution occur in the alloy and many phases remain. When the alloy was treated above 410 ~C, the eutectic phases transform into spherical shape as the I-phase turns to W-phase. After heat treatment for long time, the alloy is over burnt and the W-phase decomposes to Mg-Y binary phase.
基金
financially supported by the National Natural Science Foundation of China(Nos.50835002 and 51105102)