The effects of mesogen-jacketed liquid crystalline polymer poly(dipropyl vinylterephthalate)(PDPVT) on the mechanical and thermal properties of diglycidyl ether of bisphenol-A(DGEBA) epoxy resin were investigated by impact test, tensile test and thermogravimetric analysis(TGA). The mechanism underlying the enhancement of mechanical properties of epoxy resin was studied using 1D wide-angle X-ray diffraction(WAXD) and scanning electron microscope(SEM). It was found that the mechanical properties of 1 wt%–5 wt% PDPVT/DGEBA composites were significantly improved compared to neat epoxy resin. Especially, the epoxy resin with 3 wt% PDPVT had the greatest increase in mechanical properties, with the impact strength, tensile strength and elongation while breaking increased by 87%, 59% and 174%, respectively. The increased mechanical strength was due to the fact that PDPVT maintained liquid crystalline phase in cured PDPVT/DGEBA composites, which would blunt the crack tip and prevent crack propagation. Moreover, PDPVT had slight effect on the thermal stability properties of epoxy resin.
The effects of mesogen-jacketed liquid crystalline polymer poly（dipropyl vinylterephthalate） （PDPVT） on the mechanical and thermal properties of diglycidyl ether of bisphenol-A （DGEBA） epoxy resin were investigated by impact test, tensile test and thermogravimetric analysis （TGA）. The mechanism underlying the enhancement of mechanical properties of epoxy resin was studied using 1D wide-angle X-ray diffraction （WAXD） and scanning electron microscope （SEM）. It was found that the me- chanical properties of 1 wt%-5 wt% PDPVT/DGEBA composites were significantly improved compared to neat epoxy resin. Especially, the epoxy resin with 3 wt% PDPVT had the greatest increase in mechanical properties, with the impact strength, tensile strength and elongation while breaking increased by 87%, 59% and 174%, respectively. The increased mechanical strength was due to the fact that PDPVT maintained liquid crystalline phase in cured PDPVT/DGEBA composites, which would blunt the crack tip and prevent crack propagation. Moreover, PDPVT had slight effect on the thermal stability properties of epoxy resin.
基金
financially supported by the National Natural Science Foundation of China(51343008)