Optical and gas sensing properties of mesoporous hollow ZnO microspheres fabricated via a solvothermal method 被引量:2

Optical and gas sensing properties of mesoporous hollow ZnO microspheres fabricated via a solvothermal method
原文传递
导出
摘要 Mesoporous,hollow Zn O microspheres were synthesized via a hydrothermal method,using glycerol and zinc acetate as the starting materials.XRD and FESEM analysis showed that the surface morphology of the spheres with a Wurtzite structure could be reasonably adjusted by varying the weight ratio(Rw) of Zn(CH3COO)2 2H2O:H2O:C3H8O3.The responses of the gas sensor based on the spheres to 100 ppm ethanol and 100 ppm acetone are 18.9 and 10.4,respectively.The response and recovery times of the sensor to ethanol and acetone are 2 s and 3 s,3 s and 5 s,respectively.The hollow spheres show an intense UV emission at 392 nm and a broad blue-green emission at 488 nm.Interestingly,a light trapping phenomenon is revealed by UV emission and scattering measurements on the microspheres,which can be attributed to the mesoporous shell and hollow structure of the microsphere. Mesoporous,hollow Zn O microspheres were synthesized via a hydrothermal method,using glycerol and zinc acetate as the starting materials.XRD and FESEM analysis showed that the surface morphology of the spheres with a Wurtzite structure could be reasonably adjusted by varying the weight ratio(Rw) of Zn(CH3COO)2 2H2O:H2O:C3H8O3.The responses of the gas sensor based on the spheres to 100 ppm ethanol and 100 ppm acetone are 18.9 and 10.4,respectively.The response and recovery times of the sensor to ethanol and acetone are 2 s and 3 s,3 s and 5 s,respectively.The hollow spheres show an intense UV emission at 392 nm and a broad blue-green emission at 488 nm.Interestingly,a light trapping phenomenon is revealed by UV emission and scattering measurements on the microspheres,which can be attributed to the mesoporous shell and hollow structure of the microsphere.
出处 《Chinese Chemical Letters》 SCIE CAS CSCD 2015年第3期304-308,共5页 中国化学快报(英文版)
基金 supported by the National Natural Science Foundation of China and the Civil Aviation Administration of China (No.61079010) the financial supports of the Science and Technology Innovation Guide Funds of Civil Aviation Administration of China (2014) the Significant Preresearch Funds of Civil Aviation University of China (No.3122013P001)
关键词 hollow spheres hydrothermal microsphere attributed ethanol acetate starting glycerol FESEM hollow spheres hydrothermal microsphere attributed ethanol acetate starting glycerol FESEM
  • 相关文献

参考文献2

二级参考文献49

  • 1X.W. Lou, LA. Archer, Z. Yang, Hollow micro-/nanostructures: synthesis and applications, Adv. Mater. 20 (2008) 3987-4019. 被引量:1
  • 2j. Liu, F. Liu, j. Wu, et al., Recent developments in the chemical synthesis of inorganic porous capsules, j. Mater. Chern. 19 (2009) 6073-6084. 被引量:1
  • 3G. Rethore, A. Pandit, Use of templates to fabricate nanoscale spherical structures for defined architectural control, Small 6 (2010) 488-498. 被引量:1
  • 4j. Hu, M. Chen, X. Fang, et al., Fabrication and application of inorganic hollow spheres, Chern. Soc. Rev. 40 (2011) 5472-5491. 被引量:1
  • 5j. Liu, D. Xue, Hollow nanostructured anode materials for Li-ion batteries, Nano?scale Res. Lett. 5 (2010) 1525-1534. 被引量:1
  • 6X. Wang, W. Tian, T. Zhai, et al., Cobalt (II, III) oxide hollow structures: fabrication, properties and applications, j. Mater. Chern. 22 (2012) 23310-23326. 被引量:1
  • 7X. Lai, j.E. Halpert, D. Wang, Recent advances in micro-/nano-structured hollow spheres for energy applications: from simple to complex systems, Energy Environ. Sci. 5 (2012) 5604-5618. 被引量:1
  • 8Y. Zhao, L. jiang, Hollow microjnanomaterials with multilevel interior structures, Adv. Mater. 21 (2009) 3621-3638. 被引量:1
  • 9H. Zeng, Synthesis and self-assembly of complex hollow materials.J, Mater. Chern. 21 (2011) 7511-7526. 被引量:1
  • 10M. Yang, j. Ma, Cd, Zhang, et al., General synthetic route toward functional hollow spheres with double-shelled structures, Angew. Chern. Int. Ed. 44 (2005) 6727-6730. 被引量:1

共引文献9

同被引文献4

引证文献2

二级引证文献8

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部