摘要
阐述了超薄玻璃(<0.3 mm)化学钢化的缺陷问题,并对其产生的原因进行了分析、总结,同时提出了工艺技术和设备改造的解决方案。
The possible defects arising from chemically-strengthen of ultra-thin （under 0.3mm） glass were described and the causes of the defects were discussed . Helpful solutions were proposed from improvement of technology and equipment.
出处
《玻璃》
2015年第1期44-46,共3页
Glass
关键词
超薄玻璃
化学钢化
缺陷
ultra-thin glass, chemically-strengthen, defect