大型储层改造过程中,高速含砂流体引起的冲蚀是管柱失效的重要原因之一。利用自行研制的喷射式冲蚀实验装置,以蒸馏水和3.5 wt%Na Cl为模拟溶液,对比研究了超级13Cr钢在含砂液固两相流体中的冲蚀速率随主流速度和压裂排量的变化规律。分析了Cl^-1对超级13Cr钢的冲蚀的加速作用机理。研究表明,对于89mm×6.45 mm油管压裂,当排量低于2.2 m^3/min时,Cl^-1加速超级13Cr钢冲蚀速率作用不够明显;当排量在2.2-2.75 m^3/min时,Cl^-1使得电化学腐蚀加剧,导致总的冲蚀速率急剧增加;当排量大于2.75 m^3/min时,冲蚀速率主要由冲刷流体产生及机械作用主导,Cl^-1的影响开始降低。
Erosion caused by high speed sand fluid plays an important role in the failures of tubing string for the reservoir fracturing. The erosion rate of super- 13 Cr steel were investigated by using the self- made jet experiment device in distilled water and 3. 5wt% NaC l solution containing sand. The erosion mechanism of Cl- 1was analyzed for super- 13 Cr steel. In fracturing operation of 89 mm × 6. 45 mm oil tube,the erosion rate of Cl- 1was not obvious when the displacement was less than 2. 2m3/ min,and then increased rapidly when displacement was between 2. 2- 2. 75 m3/ min. When displacement was more than2. 75 m3/ min,the mechanical erosion dominated and the effect of Cl- 1reduced.
出处
《钻采工艺》
CAS
北大核心
2015年第1期76-78,5,共3页
Drilling & Production Technology
基金
国家重大科技专项"超深超高压气井油套管柱安全评价与控制技术研究"(编号:2011ZX05046-03-07)
中国石油科技攻关重大专项"塔里木油田勘探开发关键技术研究"(编号:2010E-2105)课题5"超深超高压高温气井试油完井及储层改造技术"
关键词
超级13Cr钢
冲蚀
含砂流体
super-13Cr steel,erosion,distilled water,3.5wt% NaCl solution