Highly mesoporous Zn O and g-Al2O3nanowires（NWs） are both synthesized by a hydrothermal method using commercially available porous anodic aluminium oxide（AAO） as template. AAO membrane acts as template for Zn O NWs and both as template and precursor for g-Al2O3 NWs. The formation of intermediate phases of porous Zn6Al2（OH）16CO3and boehmite（g-Al OOH） were observed, both occurring during the hydrothermal synthesis of porous Zn O and g-Al2O3 NWs, respectively, and disappearing after annealing at 600 C. This novel template-assisted hydrothermal process leads to the formation of porous Zn O and g-Al2O3NWs（specific surface area of 192 m2 g 1and 263 m2 g 1, respectively）, showing pore sizes around 4 nm in diameter. The influence of the reaction parameters on the nanostructure morphology was also investigated. A Zn O seed layer, deposited on the AAO channels prior to the hydrothermal synthesis, leads to more compact Zn O nanowires（99 m2 g-1） protecting the AAO host from the chemical attack of the precursor solution.
Highly mesoporous Zn O and g-Al2O3nanowires（NWs） are both synthesized by a hydrothermal method using commercially available porous anodic aluminium oxide（AAO） as template. AAO membrane acts as template for Zn O NWs and both as template and precursor for g-Al2O3 NWs. The formation of intermediate phases of porous Zn6Al2（OH）16CO3and boehmite（g-Al OOH） were observed, both occurring during the hydrothermal synthesis of porous Zn O and g-Al2O3 NWs, respectively, and disappearing after annealing at 600 C. This novel template-assisted hydrothermal process leads to the formation of porous Zn O and g-Al2O3NWs（specific surface area of 192 m2 g 1and 263 m2 g 1, respectively）, showing pore sizes around 4 nm in diameter. The influence of the reaction parameters on the nanostructure morphology was also investigated. A Zn O seed layer, deposited on the AAO channels prior to the hydrothermal synthesis, leads to more compact Zn O nanowires（99 m2 g-1） protecting the AAO host from the chemical attack of the precursor solution.