摘要
Un-doped and Co-doped ZnO nanoparticles （NPs） with different weight ratios （0.5, 1.0, 1.5, and 2.0 wt% of Co） were synthesized by a facile and rapid microwave-assisted combustion method using urea as a fuel. The prepared NPs were characterized by X-ray diffraction （XRD）, high resolution scanning electron microscopy （HR-SEM）, energy dispersive X-ray analysis （EDX）, diffuse reflectance spectroscopy （DRS）, photoluminescence （PL） spectroscopy and vibrating sample magnetometry （VSM）. XRD patterns refined by the Rietveld method indicated that Co-doped ZnO had a single pure phase with wurtzite structure suggesting that Co^2＋ ions would occupy Zn^2＋ ionic sites within the ZnO crystal lattice. Interestingly, the morphology was found to convert substantially from grains to nanoparticles with close-packed periodic array of hexagonal-like shape and then into randomly distributed spherical NPs with the variation of Co-content. The optical band gap estimated using DRS was found to be red-shifted from 3.22 eV for the un-doped ZnO NPs then decrease up to 2.88 eV with increasing Co-content. PL spectra showed a strong green emission band thus confirming the formation of pure single ZnO phase. Magnetic studies showed that Co-doped ZnO NPs exhibited room temperature ferromagnetism （RTFM） and that the saturation magnetization attained a maximum value of 2.203 × 10^-3 emu/g for the highest Co-content. The antibacterial studies performed against a set of bacterial strains showed that the 2.0 wt% Co-doped ZnO NPs possessed a greater antibacterial effect.
Un-doped and Co-doped ZnO nanoparticles （NPs） with different weight ratios （0.5, 1.0, 1.5, and 2.0 wt% of Co） were synthesized by a facile and rapid microwave-assisted combustion method using urea as a fuel. The prepared NPs were characterized by X-ray diffraction （XRD）, high resolution scanning electron microscopy （HR-SEM）, energy dispersive X-ray analysis （EDX）, diffuse reflectance spectroscopy （DRS）, photoluminescence （PL） spectroscopy and vibrating sample magnetometry （VSM）. XRD patterns refined by the Rietveld method indicated that Co-doped ZnO had a single pure phase with wurtzite structure suggesting that Co^2＋ ions would occupy Zn^2＋ ionic sites within the ZnO crystal lattice. Interestingly, the morphology was found to convert substantially from grains to nanoparticles with close-packed periodic array of hexagonal-like shape and then into randomly distributed spherical NPs with the variation of Co-content. The optical band gap estimated using DRS was found to be red-shifted from 3.22 eV for the un-doped ZnO NPs then decrease up to 2.88 eV with increasing Co-content. PL spectra showed a strong green emission band thus confirming the formation of pure single ZnO phase. Magnetic studies showed that Co-doped ZnO NPs exhibited room temperature ferromagnetism （RTFM） and that the saturation magnetization attained a maximum value of 2.203 × 10^-3 emu/g for the highest Co-content. The antibacterial studies performed against a set of bacterial strains showed that the 2.0 wt% Co-doped ZnO NPs possessed a greater antibacterial effect.