The visible-light photochromic hybrid film was constructed by entrapping phosphomolybdic acid（PMoA） into polyvinylpyrrolidone（PVPd） networks. The microstructure, photochromic properties and mechanism were inves- tigated with transmission electron microscopy（TEM）, atomic force microscopy（AFM）, Fourier transform infrared （FTIR） spectroscopy, ultraviolet-visible（UV-Vis） spectra and X-ray photoelectron spectroscopy（XPS）. The results in- dicate that the Keggin geometry of PMoA and the basic structure of PVPd are not destroyed during the composite process. Irradiated with visible light, the transparent PMoA/PVPd film changes color from colorless to blue and ex- hibits reversible photochromism in the presence of oxygen. According to the XPS analysis, the charge-transfer bridge of N-H-O has been built between PMoA and PVPd matrix via non-covalent bonding, and the appearance of Mo5＋ species indicates that the photo-reduction process is in accordance with the proton transfer mechanism.
The visible-light photochromic hybrid film was constructed by entrapping phosphomolybdic acid（PMoA） into polyvinylpyrrolidone（PVPd） networks. The microstructure, photochromic properties and mechanism were inves- tigated with transmission electron microscopy（TEM）, atomic force microscopy（AFM）, Fourier transform infrared （FTIR） spectroscopy, ultraviolet-visible（UV-Vis） spectra and X-ray photoelectron spectroscopy（XPS）. The results in- dicate that the Keggin geometry of PMoA and the basic structure of PVPd are not destroyed during the composite process. Irradiated with visible light, the transparent PMoA/PVPd film changes color from colorless to blue and ex- hibits reversible photochromism in the presence of oxygen. According to the XPS analysis, the charge-transfer bridge of N-H-O has been built between PMoA and PVPd matrix via non-covalent bonding, and the appearance of Mo5＋ species indicates that the photo-reduction process is in accordance with the proton transfer mechanism.
基金
Supported by the National Natural Science Foundation of China（No.61340048）, the Specialized Research Fund for the Doc- toral Program of Higher Education of China（No.20110041120001） and the Industrial Technology Research and Development Project of Jilin Province, China（No.2013C044）.