碳含量及其结构对 SiOC 陶瓷纤维抗氧化性的影响 被引量:1

Effects of carbon content and structure on oxidation resistance of silicon oxycarbide fiber
下载PDF
导出
摘要 以乙烯基三甲氧基硅烷(VTMS)、正硅酸乙酯(TEOS)和苯基三甲氧基硅烷(PTMS)为原料,采用溶胶-凝胶法制备出了致密的 SiOC 纤维.研究结果表明,通过在 VTMS 中加入不同比例的 TEOS 或者 PT-MS 可以把 SiOC 陶瓷纤维的碳含量在21.8%~30.1%之间调节.纤维中碳的含量和结构对其抗氧化性有显著影响.抗氧化性随着碳含量和碳畴尺寸的增加而下降,以75% VTMS-25% TEOS 为原料制备的SiOC 陶瓷纤维在空气中氧化时可以在纤维表面形成致密的氧化膜,降低氧扩散速度,使该纤维具有良好的抗氧化性. Silicon oxycarbide fibers were prepared from vinyltrimethoxysilane (VTMS ), tetraethoxysilane (TEOS)and phenyltrimethoxysilane (PTMS)by sol-gel method.It was found that the carbon content of the silicon oxycarbide fibers can be adjusted from 21.8% to 30.1wt% by change the mole ratio of VTMS,TEOS and PTMS in the precursors.The oxidation resistance of the fibers was impacted by the content and structure of carbon.The oxidation resistance decreased with the increasing content and domain size of the carbon.Silicon oxycarbide fibers prepared with 75%VTMS-25% TEOS showed good oxidation resistance in air at 600 ℃,be-cause a thin and dense silica film was formed on the surface of the fibers,preventing fibers from further oxida-tion.
出处 《功能材料》 EI CAS CSCD 北大核心 2014年第15期15084-15088,共5页 Journal of Functional Materials
基金 国家自然科学基金资助项目(51072169)
关键词 溶胶-凝胶法 陶瓷纤维 抗氧化性 硅氧碳 自由碳 sol-gel method ceramic fiber oxidation resistance silicon oxycarbide free carbon
  • 相关文献

参考文献2

二级参考文献24

  • 1赵一阳,王海鹰,李响,杨洋,杨敏,王策.静电纺丝法制备硫酸化的二氧化锆/二氧化硅复合纤维[J].高等学校化学学报,2007,28(2):382-384. 被引量:9
  • 2Cooke T F. Inorganic fibers - a literature review [J]. J Am Ceram Soc, 1991, 74(12): 2959 2978. 被引量:1
  • 3Yajima S, Hasegama Y, Hayasbi J, et al. Synthesis of continuous silicon carbide iber with high tensile strength and high Young's modulus, bosilane as precursor [J]. J 2576. part 1 synthesis of polycar Mater Sci, 1978, 13:2569. 被引量:1
  • 4Hasegawa Y, Iimura M, Yaiima S. Synthesis of continu- ous silicon carbide fiber, part 2 conversion of polycarbosi- lane fiber into silicon carbide fibers [J]. J Mater Sci, 1980, 15: 720-728. 被引量:1
  • 5Hasegawa Y. Synthesis of continuous silicon carbide i ber, part 3 pyrolysis process of polycarbosilane and struc tureofthe products [J]. J Mater Sci, 1983, 18: 3633 3648. 被引量:1
  • 6Hasegawa Y. Synthesis of continuous silicon carbide fi-her, part 4 the structure oi polycarbosllane as the precur- [J] sor . J Mater Sci, 1986, 21: 321-328. 被引量:1
  • 7Ichikawa H, Machibo F, Mitsuno S, et al. Synthesis of continuous silicon carbide fiber, part 5 factors affecting stability of polycarbosilane to oxidation [J]. J Mater Sei, 1986, 21: 4352-4358. 被引量:1
  • 8Hasegawa Y. Synthesis of continuous silicon carbide fi- ber, part 6 pyrolysis process of cured polycarbosilane fi- ber and structure of SiC fiber [J]. J Mater Sci, 1989, 24: 1177-1190. 被引量:1
  • 9Suwardie H, Kalyon D M, Kovenklioglu S. Thermal behavior and curing kinetics of poly(carbosilane) [J]. JAppl Polym Sci, 1991, 42:1087-1095. 被引量:1
  • 10Narisawa M, Shimoda M, Okamura K, et al. Reaction mechanism of the pyrolysis of polycarbosilane and poly- carbosilazane as ceramic precursors [J]. Bull Chem Soe Jpn, 1995, 68: 1098-1104. 被引量:1

共引文献8

同被引文献2

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部