摘要
在挂锤式拉伸试验机上对LY12CZ铝合金进行了超塑性试验 ,研究了其应变速率变化规律。试验结果发现 ,在恒载荷下最初应变速率变形的时间只有 4 0～ 6 0min ,随后 ,应变速率会自动增加 ,试样断裂时的应变速率比初始应变速率增加了一倍左右。
Super plastic deformation of LY12CZ aluminum alloy was tested on tensile machine with hung hammer and the law of strain rate change was studied.The results show that when the load is constant,the time in initial strain rate deformation is only 40 to 60 minutes,after then,the strain rate increases automatically.When sample is break off,the strain rate is double of the initial one.