Mesoporous single crystal-like Y2O3 nanocubes have been prepared through a coordination-based self- assembly process. Firstly, a uniform nanocube-like Y-lysine precursor was simply prepared with hydrothermal treatment. After the simple thermal treatment process, nanocube-shaped yttrium oxides with the morphology inherited from the Y-lysine precursor were successfully prepared. The phase, morphology, size and crystalline structure were well characterized by XRD, SEM and TEM. N2 adsorption-desorption demonstrates the mesoporous characteristics of the Y2O3 nanocubes, showing a relatively high surface area of 60 m^2/g.
Mesoporous single crystal-like Y2O3 nanocubes have been prepared through a coordination-based self- assembly process. Firstly, a uniform nanocube-like Y-lysine precursor was simply prepared with hydrothermal treatment. After the simple thermal treatment process, nanocube-shaped yttrium oxides with the morphology inherited from the Y-lysine precursor were successfully prepared. The phase, morphology, size and crystalline structure were well characterized by XRD, SEM and TEM. N2 adsorption-desorption demonstrates the mesoporous characteristics of the Y2O3 nanocubes, showing a relatively high surface area of 60 m^2/g.
基金
supported by NSFC(No.21373116)
Tianjin Natural Science Research Fund(No.13JCYBJC18300)
RFDP(No. 20120031110005)
MOE Innovation Team(No.IRT13022) of China