摘要
The solid state morphology of the tri block copolymer PS b PCEMA b PtBA, which was synthesized by anionic polymerization with narrow molecular weight distribution, was in lamella structure from TEM micrographs. After being blended with polystyrene with the mass ratio of 1∶0 4, the morphology showed cylinder structure. With PS as continous phase, PCEMA and PtBA phases formed cylinders with PCEMA as outer layer. The nanofibres can be got and dispersed in good solvents of PS when the PCEMA phase was crosslinked. The t butyl group in PtBA phase can be cleavaged by reacting with TMSI, and nanofibres changed to nanotubes finally. It has the great potential applications, such as in the preparation of nanowires, template polymerization, nano reactor etc ..
The solid state morphology of the tri block copolymer PS b PCEMA b PtBA, which was synthesized by anionic polymerization with narrow molecular weight distribution, was in lamella structure from TEM micrographs. After being blended with polystyrene with the mass ratio of 1∶0 4, the morphology showed cylinder structure. With PS as continous phase, PCEMA and PtBA phases formed cylinders with PCEMA as outer layer. The nanofibres can be got and dispersed in good solvents of PS when the PCEMA phase was crosslinked. The t butyl group in PtBA phase can be cleavaged by reacting with TMSI, and nanofibres changed to nanotubes finally. It has the great potential applications, such as in the preparation of nanowires, template polymerization, nano reactor etc ..
出处
《高等学校化学学报》
SCIE
EI
CAS
CSCD
北大核心
2002年第1期158-160,共3页
Chemical Journal of Chinese Universities