Mechanical properties of poly (vinyl chloride) film doped with micro rare earth neodymium are improved notably. Its tensile strength increases from 36 1 to 52 9 MPa, while its flexibility is increased significantly by adding active silanol extracted from water glass. Both ultraviolet and microwave crosslinking result in samples with satisfactory mechanical properties, and the flexibility of the microwave crosslinked samples is much higher than that of the ultraviolet crosslinked ones.
Mechanical properties of poly (vinyl chloride) film doped with micro rare earth neodymium are improved notably. Its tensile strength increases from 36 1 to 52 9 MPa, while its flexibility is increased significantly by adding active silanol extracted from water glass. Both ultraviolet and microwave crosslinking result in samples with satisfactory mechanical properties, and the flexibility of the microwave crosslinked samples is much higher than that of the ultraviolet crosslinked ones.
出处
《中国稀土学报》
CAS
CSCD
北大核心
2001年第5期463-464,共2页
Journal of the Chinese Society of Rare Earths
基金
江苏省留学归国人员科研基金 (D0 0 0 92 17)