Yttria-stabilized zirconia （YSZ） is irradiated with 2.0-MeV Au2＋ ions and 30-keV He＋ ions. Three types of He, Au, Au ＋ He （successively） ion irradiation are performed. The maximum damage level of a sequential dual ion beam implanted sample is smaller than single Au ion implanted sample. A comparable volume swelling is found in a sequential dual ion beam irradiated sample and it is also found in a single Au ion implanted sample. Both effects can be explained by the partial reorganization of the dislocation network into weakly damaged regions in the dual ion beam implanted YSZ. A vacancy-assisted helium trapping/diffusion mechanism in the dual ion beam irradiated condition is discussed. No phase transformation or amorphization behavior happens in all types of ion irradiated YSZ.
Yttria-stabilized zirconia （YSZ） is irradiated with 2.0-MeV Au2＋ ions and 30-keV He＋ ions. Three types of He, Au, Au ＋ He （successively） ion irradiation are performed. The maximum damage level of a sequential dual ion beam implanted sample is smaller than single Au ion implanted sample. A comparable volume swelling is found in a sequential dual ion beam irradiated sample and it is also found in a single Au ion implanted sample. Both effects can be explained by the partial reorganization of the dislocation network into weakly damaged regions in the dual ion beam implanted YSZ. A vacancy-assisted helium trapping/diffusion mechanism in the dual ion beam irradiated condition is discussed. No phase transformation or amorphization behavior happens in all types of ion irradiated YSZ.
基金
supported by the National Basic Research and Development Program of China(Grant Nos.2010CB832904 and 2010CB832902)
the National Natural Science Foundation of China(Grant No.91226202)