目的研制一种新型木塑复合材料。方法采用对比试验及验证试验，合理设计新型木塑复合材料的配方及其制备方法。结果确定了新型木塑复合材料的最佳配方和最优的制备方法及工艺参数（板材厚度为12mm，混料加热温度为80～90℃，冷却水的温度为3～8℃）。结论研制成功的新型木塑复合材料具有抗静电、阻燃防火、附着力强、防潮、防水、防虫、防霉、耐腐蚀、强度高、韧性好、耐老化、缓冲性能好、表面光滑、质量轻、木质感强、无污染、价格低等优良性能，适合印刷标志。
Objective To develop a new type of wood-plastic composite material. Methods The formula and the preparation method of a new type of wood-plastic composite material were reasonably designed by comparison test and verification test. Results The optimal formula of a new type of wood-plastic composite material and the most optimized preparation method and technological parameters （plate thickness： 12 mm, heating temperature of material mixing： 80 - 90 ℃, temperature of cooling water： 3 - 8 ℃ ） were determined. Conclusion The new type of wood-plastic composite material was anti-static, fire-proo- fing, moisture proof, water proof, insect preventing, mould proof, and had strong adhesive force, high corrosion resistance, high strength, good tenacity, high aging resistance, good buffering effects, smooth surface, light weight , good woody performance , with no pollution and low cost, and is therefore suitable for printing marks.
出处
《包装工程》
CAS
CSCD
北大核心
2014年第3期137-142,共6页
Packaging Engineering
关键词
新型木塑复合材料
配方
制备方法
研究
new type of wood-plastic composite material
formula
preparation method
research