Characterization of ceramic coating on ZK60 magnesium alloy prepared in a dual electrolyte system by micro-arc oxidation 被引量:8

Characterization of ceramic coating on ZK60 magnesium alloy prepared in a dual electrolyte system by micro-arc oxidation
下载PDF
导出
摘要 Micro-arc oxidation (MAO) process was cartied out in an optimized dual electrolyte system to fabricate a compact, smooth, and corrosion resistant coating on ZK60 Mg alloy. The microstructural characteristics of coating were investigated by scanning electron microscopy (SEM) coupled with an energy dispersive spectrometer (EDS) and X-ray diffraction (XRD). Test of mass loss was conducted at a 3.5 % NaCl solution to assess the resistance to corrosion. The bonding strength between the coating and ZK60 substrate was evaluated using scratch experiment. The results reveal that MgA1204 and MgO are the main phases of ceramic coating obtained in the dual electrolyte system. The corrosion rate of coating prepared in the optimized dual electrolyte is only 0.0061 g.m-2.h-1, which demonstrates excellent corrosion resistance. This is mainly due to the compact, uniform coating with high bonding strength. Micro-arc oxidation (MAO) process was cartied out in an optimized dual electrolyte system to fabricate a compact, smooth, and corrosion resistant coating on ZK60 Mg alloy. The microstructural characteristics of coating were investigated by scanning electron microscopy (SEM) coupled with an energy dispersive spectrometer (EDS) and X-ray diffraction (XRD). Test of mass loss was conducted at a 3.5 % NaCl solution to assess the resistance to corrosion. The bonding strength between the coating and ZK60 substrate was evaluated using scratch experiment. The results reveal that MgA1204 and MgO are the main phases of ceramic coating obtained in the dual electrolyte system. The corrosion rate of coating prepared in the optimized dual electrolyte is only 0.0061 g.m-2.h-1, which demonstrates excellent corrosion resistance. This is mainly due to the compact, uniform coating with high bonding strength.
出处 《Rare Metals》 SCIE EI CAS CSCD 2013年第5期459-464,共6页 稀有金属(英文版)
基金 supported by the Priority Academic Program Development of Jiangsu Higher Education Institutions and the Key Laboratory of Advanced Welding Technology of Jiangsu Province, China (No. JSAWT-11)
关键词 ZK60 magnesium alloys Micro-arc oxidation CHARACTERIZATION Dual electrolyte system ZK60 magnesium alloys Micro-arc oxidation Characterization Dual electrolyte system
  • 引文网络
  • 相关文献

参考文献2

二级参考文献5

  • 1[7]Michelmore A, Gong W, Jenkins P, et al. The influence of polyphosphates in modifying the surface behavito and inter actions of metal oxide particles[A]. In: Laskouski J S. Polymers in Mineral Processing[C]. Quebec City, 1999. 231-245. 被引量:1
  • 2[8]Parfitt R L, Atkinson R J, Smart R S C. The mechanism of phosphate fixation by ironoxides[J]. Soil Sci Soc Am Proc, 1975, 39: 837-841. 被引量:1
  • 3[9]Parfitt R L, Russell J D, Farmer V C. Comfirmation of the surface structure of goetyhite and phosphated goethite by infrared speetroscopy[J]. J Chem Soc Faraday Trans, 1976, 172: 1082-1087. 被引量:1
  • 4[10]Gong W Q. A real-time in-situ ATR-FITIR spectroscopic study of linear phosphate on titania surfaces[J]. Int J Miner Process, 2001, 63: 147-165. 被引量:1
  • 5[12]Flory P J, Statistical Mechanics of Chain Molecules[M].New York: Wiley-Interscience, 1969. 被引量:1

共引文献33

同被引文献121

引证文献8

二级引证文献25

相关主题

;
使用帮助 返回顶部