在二钼酸铵(ADM)蒸发结晶的过程中,加入了十六烷基三甲基溴化铵(CTAB)及十二烷基硫酸钠(SDS).结果表明,加入CTAB的ADM颗粒明显长大,优于加入SDS的颗粒,加入2%CTAB时,产物ADM颗粒可增大至1 mm,达到了市场的要求.
In the evaporation crystallization process of ammonium dimolybdate （ ADM）, hexadecyl trimethyl ammonium bromide （CTAB） and sodium dodecyl sulfate （SDS） were added to the solution respectively. The re- sults show that CTAB can better control the size of ADM particles than SDS. The ADM particles can grow to 1 mm and meet the market requirements, when 2% CTAB added.