摘要
Two new coordination polymers,[Zn（bdc）（1,3-bimb）]n（1） and {[Mn2（ox）2（1,3,5tib）4/3]·4H2O}n（2）（H2ox = oxalic acid,H2bdc = terephthalic acid,1,3-bimb = 1,3-bis（imidazol-1ylmethyl）benzene,1,3,5-tib = 1,3,5-tri（imidazol-1-yl）benzene）,were synthesized and characterized by elemental analysis,IR,powder X-ray diffraction（PXRD）,and thermogravimetric（TG） analyses.X-ray diffracation analysis reveals that two kinds of zigzag chains [Zn（bdc）]n and [Zn（1,3-bimb）]n in compound 1 are interweaved to form a 3D 4-fold interpenetrated 66-dia framework.In compound 2,Mn（1） and Mn（2） are linked via 1,3,5-tib ligands to form two different nets of [Mn6（1,3,5-tib）6 ]n along the ab plane with inner-or outer-shape N–Mn–N angles,which are connected by 1D infinite [Mn2（ox）2 ]n chains via Mn–O bonds to result in a（3,3,3,4,4）-connected（4·8·10）3（4·82）3（4·83·102）6（82·104·3）3（83）4 topology.Moreover,the photoluminescence of 1 has been investigated.The crystal of 1 crystallizes in orthorhombic,space group Pna2 with a = 13.2267（6）,b = 9.1717（4）,c = 17.4492（8）,V = 2116.79（16）3,Z = 4,C22 H18N4O4 Zn,Mr = 467.77,Dc = 1.468 g/cm3,F（000） = 960 and μ（MoKα） = 1.197 mm-1.The final R = 0.0280 and wR = 0.0618 for 3695 observed reflections with I 2（I） and R = 0.0389 and wR = 0.0653 for all data.The crystal of 2 crystallizes in rhombohedral,space group R-3 with a = 22.080（8）,c = 31.19（2）,V = 13167（11） 3,Z = 18,C24 H25 Mn2 N8 O13,Mr = 743.40,Dc = 1.688 g/cm3,F（000） = 6822 and μ（MoKα） = 0.945 mm-1.The final R = 0.0429 and wR = 0.1035 for 5160 observed reflections with I 2（I） and R = 0.0824 and wR = 0.1244 for all data.
Two new coordination polymers,[Zn（bdc）（1,3-bimb）]n（1） and {[Mn2（ox）2（1,3,5tib）4/3]·4H2O}n（2）（H2ox = oxalic acid,H2bdc = terephthalic acid,1,3-bimb = 1,3-bis（imidazol-1ylmethyl）benzene,1,3,5-tib = 1,3,5-tri（imidazol-1-yl）benzene）,were synthesized and characterized by elemental analysis,IR,powder X-ray diffraction（PXRD）,and thermogravimetric（TG） analyses.X-ray diffracation analysis reveals that two kinds of zigzag chains [Zn（bdc）]n and [Zn（1,3-bimb）]n in compound 1 are interweaved to form a 3D 4-fold interpenetrated 66-dia framework.In compound 2,Mn（1） and Mn（2） are linked via 1,3,5-tib ligands to form two different nets of [Mn6（1,3,5-tib）6 ]n along the ab plane with inner-or outer-shape N–Mn–N angles,which are connected by 1D infinite [Mn2（ox）2 ]n chains via Mn–O bonds to result in a（3,3,3,4,4）-connected（4·8·10）3（4·82）3（4·83·102）6（82·104·3）3（83）4 topology.Moreover,the photoluminescence of 1 has been investigated.The crystal of 1 crystallizes in orthorhombic,space group Pna2 with a = 13.2267（6）,b = 9.1717（4）,c = 17.4492（8）,V = 2116.79（16）3,Z = 4,C22 H18N4O4 Zn,Mr = 467.77,Dc = 1.468 g/cm3,F（000） = 960 and μ（MoKα） = 1.197 mm-1.The final R = 0.0280 and wR = 0.0618 for 3695 observed reflections with I 2（I） and R = 0.0389 and wR = 0.0653 for all data.The crystal of 2 crystallizes in rhombohedral,space group R-3 with a = 22.080（8）,c = 31.19（2）,V = 13167（11） 3,Z = 18,C24 H25 Mn2 N8 O13,Mr = 743.40,Dc = 1.688 g/cm3,F（000） = 6822 and μ（MoKα） = 0.945 mm-1.The final R = 0.0429 and wR = 0.1035 for 5160 observed reflections with I 2（I） and R = 0.0824 and wR = 0.1244 for all data.
基金
Supported by the National Natural Science Foundation of China(20873150)
Natural Science Foundation of Shandong Province(ZR2010BQ023)