摘要
本文通过对可伐合金应力腐蚀断口的微观特征的研究 ,证明了可伐合金为氢脆敏感性材料 ,H+、Cl-浓度增加 ,合金易发生腐蚀开裂。
Through an analysis of the micro-properties of stress corrosion fracture of Kovar alloy,the paper proves that this alloy is a material sensitive to hydrogen brittleness and that the more the concentration of H + and Cl -,the easier the occurrence of the corrosion fracture.