3-Aminopropyltriethoxysilane functionalized worm-like mesoporous silica monolithic（WMSM-NH2） was prepared and used as a new regenerable adsorbent for the removal of Cu2＋ ions. The analysis results show that the WMSM-NH2 monolithic had a high efficiency value of 99.3% for Cu2＋ remediation when the Cu2＋ solution was at an initial concentration of 10.32 mg/L. The regeneration study of the WMSM-NH2 monolithic presented that the adsorp- tion efficiency of 89.0% was remained and a mass of 92.0% was left after seven adsorption-desorption cycles were executed. The monolithic material with high resistance to the acid and good mechanical stability can facilitate the operations of adsorption and regeneration of the adsorbent.
3-Aminopropyltriethoxysilane functionalized worm-like mesoporous silica monolithic（WMSM-NH2） was prepared and used as a new regenerable adsorbent for the removal of Cu2＋ ions. The analysis results show that the WMSM-NH2 monolithic had a high efficiency value of 99.3% for Cu2＋ remediation when the Cu2＋ solution was at an initial concentration of 10.32 mg/L. The regeneration study of the WMSM-NH2 monolithic presented that the adsorp- tion efficiency of 89.0% was remained and a mass of 92.0% was left after seven adsorption-desorption cycles were executed. The monolithic material with high resistance to the acid and good mechanical stability can facilitate the operations of adsorption and regeneration of the adsorbent.
基金
Supported by the National Natural Science Foundation of China（Nos. 50573030 and 21171065）.