摘要
采用直流电位降(DCPD)方法,实现了模拟核电站高温高压水环境中的国产锻造态核级管材316L不锈钢应力腐蚀裂纹扩展速率的实时检测.断口观察表明,国产316L不锈钢在高温高压水环境中表现出明显的沿晶应力腐蚀开裂(IGSCC)行为.降低溶解O含量,增加溶解H含量能够显著降低应力腐蚀裂纹扩展速率;梯形波载荷下的裂纹扩展速率大于恒载荷下的扩展速率,裂纹扩展速率随着(t_(fl)=t_(rs))/t_h比值的增加而升高.
Stress corrosion cracking growth rates of domestic forged nuclear grade 316L stainless steel （SS） were successfully measured in high temperature and high pressure water at various temper- atures and under various loading mode. A direct current potential drop （DCPD） technique was used to monitor the crack growth throughout the test. The crack growth rate decreases with the increasing dissolved hydrogen content and the decreasing dissolved oxygen content. The crack growth rate under trapezoidal loading mode is bigger than that under constant loading. The fracture surface has typical intergranular stress corrosion cracking （IGSCC） characteristics.
出处
《金属学报》
SCIE
EI
CAS
CSCD
北大核心
2013年第8期911-916,共6页
Acta Metallurgica Sinica
基金
国家科技重大专项课题项目2011ZX06004-002
国家自然科学基金项目51025104资助~~
关键词
直流电位降
国产锻造态核级管材316L不锈钢
高温高压水
应力腐蚀裂纹扩展速率
direct current potential drop （DCPD）, domestic forged nuclear grade 316L stainlesssteel, high temperature and high pressure water, stress corrosion crack growth rate