PANI/PVDF-PEO复合材料的制备及性能研究

Preparation and Performance Research of PANI/PVDF-PEO Composite Material
下载PDF
导出
摘要 采用微乳液聚合法制备聚苯胺颗粒,并用流延法制备导电聚苯胺复合材料。利用SEM与TEM对导电聚苯胺形貌进行了分析,可知其尺寸为长100~200nm,宽30~50nm左右,形状为棒状。利用红外测试分析表明制备的聚苯胺为中间氧化态的聚苯胺。复合材料的介电性能测试说明导电聚苯胺的渗流阈值为0.13,此时介电常数与介电损耗均发生突变。本实验提高了复合材料的介电常数,在高储能密度电介质材料方面有广阔的应用。 PANI particles were prepared by microemulsion polymerization method and conductive PANI composites were prepared using this particles. Characterization results shows that conductive PANI was rod -like particles whose length was 100 to 200nm and width was 30 to 50 nm. IR shows that conductive PANI was intermediate oxidation state. The dielectric test shows that percolation threshold of conductive PANI in PVDF - PEO composite material is 0. 13. Whlie reaching this percolation threshold, the dielectric constant and dielectric loss were mutated. In this study, the dielectric constant of the composite has gready improved, it has a wide application in high energy density dielectric material.
出处 《山东化工》 CAS 2013年第6期1-3,共3页 Shandong Chemical Industry
基金 山东科技发展计划项目(2011GGX10201)
关键词 导电聚苯胺 渗流阈值 介电常数 介电损耗 conductive polyaniline percolation threshold dielectric constant dielectric loss
  • 相关文献

参考文献9

  • 1关振铎 张中太 焦金生.无机材料物理性能[M].北京:清华大学出版社,2002.212-213. 被引量:22
  • 2Kuo D H, Chang C C, Wang W K, et al. Dielectric behaviors of multi - doped BaTiO3/epoxy composites [ J ]. Journal of the European Ceramic Society 2001, 21 (9) : 1171 - 1177. 被引量:1
  • 3Wang C M, Kao K S, Lin S Y, et al. Processing and properties of CaCu3 Ti4 O12 ceramics [ J ]. Journal of Physics and Chemistry of Solids 2008, 69 (2/5) : 608 - 610. 被引量:1
  • 4段春英,周静芳,吴志申,党鸿辛.聚苯乙烯/Ag核壳结构纳米微粒的制备及表征[J].物理化学学报,2003,19(11):1049-1053. 被引量:14
  • 5李杰,韦平,汪根林,江平开.高介电复合材料及其介电性能的研究[J].绝缘材料,2003,36(5):3-6. 被引量:38
  • 6Li Q, Xue. Q z, Hao L Z, et al. Large dielectric constant of the chemically functionalized carbon nanotube/polymer composites[ J]. Composites Science and Technology 2008 ; 68 (10 - 11 ) :2290 - 2296. 被引量:1
  • 7Asturians G E, MacDiarmid, McCall R P, et al. The oxidation state of " emeraldine" base [ J ]. Synthetic Metals. 1989,29 ( 1 ) : 157 - 162. 被引量:1
  • 8Chan H L W, Zhang Q Q, Choy G L. Dielectric permittivity of PCLT/PVDF - TRFE nanocomposites [ J ]. Dielectrics and Electrical Insulation, 2007,7 ( 2 ) : 204 - 207. 被引量:1
  • 9Huang C, Zhang Q M, Su J. High -dielectric -constant all- polymer percolative composites [ J ]. Applied Physics Letters,2003,82 (20) : 3502 - 3504. 被引量:1

二级参考文献16

共引文献71

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部