摘要
A new structural phase of MgV2O6 was obtained by a high-pressure, high-temperature （HPHT） synthesis method. The new phase was investigated by the Rietveld analysis of X-ray powder diffraction data, showing space group Pbcn （No. 60） symmetry and a = 13.6113（6）A （1A =0.1 nm）, b = 5.5809（1）A, c = 4.8566（3）A, V = 368.93（2）A3 （Z = 4）. High pressure behavior was studied by Raman spectroscopy at room temperature. Under 22.5 GPa, there was no sign of a structural phase transition in the spectra, demonstrating stability of the HPHT phase up to the highest pressure.
A new structural phase of MgV2O6 was obtained by a high-pressure, high-temperature （HPHT） synthesis method. The new phase was investigated by the Rietveld analysis of X-ray powder diffraction data, showing space group Pbcn （No. 60） symmetry and a = 13.6113（6）A （1A =0.1 nm）, b = 5.5809（1）A, c = 4.8566（3）A, V = 368.93（2）A3 （Z = 4）. High pressure behavior was studied by Raman spectroscopy at room temperature. Under 22.5 GPa, there was no sign of a structural phase transition in the spectra, demonstrating stability of the HPHT phase up to the highest pressure.
基金
supported by the National Natural Science Foundation of China (Grant No. 51172091)
the Program for New Century Excellent Talents in University