AZ31B镁合金薄板交流TIG焊接接头组织和性能研究 被引量:3

Microstructure and mechanical properties of welded joint for magnesium alloy AZ31B plates by AC TIG welding
下载PDF
导出
摘要 采用交流TIG焊对2.0mm厚的变形镁合金AZ31B薄板进行焊接试验,利用扫描电镜、能谱分析、剪切试验对焊接接头的显微组织、元素分布、断口形貌、接头强度等进行分析。结果表明,焊缝区镁元素存在一定的氧化烧损,焊缝剪切强度为21MPa,剪切强度值较低,焊缝接头断口有明显的河流花样,呈现脆性准解理断裂形式。 The AC TIG welding test of magnesium alloy AZ31B plates with the thickness of 2.0 mm was carried out. The microstructure,element distribution,fracture morphology,joint strength were investigated by scanning electron microscope, energy spectrum analysis,shear test of welded joint. The results show that magnesium element in welded zone has certain oxidation loss,the shear strength of welded joint is as low as 21 MPa. The fracture surface is brittle quasi cleavage fracture, which is characterized by river pattern.
出处 《兵器材料科学与工程》 CAS CSCD 北大核心 2013年第3期66-68,共3页 Ordnance Material Science and Engineering
基金 重庆工业职业技术学院校级科研项目(GZY201106-YK)
关键词 AZ31B 镁合金 TIG 微观组织 剪切强度 AZ31B magnesium alloy TIG microstructure shear strength
  • 相关文献

参考文献7

二级参考文献31

共引文献51

同被引文献39

引证文献3

二级引证文献8

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部