A hydrometallurgical process for the recovery of cobalt oxalate from spent lithium-ion batteries was used to recycle cobalt compound by using alkali leaching, reductive acid leaching and chemical deposition of cobalt oxalate. The recycled cobalt oxalate was used to synthesize nano-Co3O4 anode material by sol-gel method. The samples were characterized by thermal gravity analysis and differential thermal analysis （TGA/DTA）, X-ray diffraction （XRD）, scanning electron microscopy （SEM） and charge/discharge measurements. The influence of molar ratio of Co2＋ to citric acid and calcination temperature on the structure and electrochemical performance of nano-Co3O4 was evaluated. As the molar ratio of Co2＋ to citric acid is 1：1, the face-centered cubic （fcc） Co3O4 powder shows the discharge capacity of 760.9 mA h g-1, the high coulombic efficiency of 99.7% in the first cycle at the current density of 125 mA g-l, and the excellent cycling performance with the reversible capacity of 442.3 mA h g-1 after 20 cycles at the current density of 250 mA g-1.
A hydrometallurgical process for the recovery of cobalt oxalate from spent lithium-ion batteries was used to recycle cobalt compound by using alkali leaching, reductive acid leaching and chemical deposition of cobalt oxalate. The recycled cobalt oxalate was used to synthesize nano-Co3O4 anode material by sol-gel method. The samples were characterized by thermal gravity analysis and differential thermal analysis （TGA/DTA）, X-ray diffraction （XRD）, scanning electron microscopy （SEM） and charge/discharge measurements. The influence of molar ratio of Co2＋ to citric acid and calcination temperature on the structure and electrochemical performance of nano-Co3O4 was evaluated. As the molar ratio of Co2＋ to citric acid is 1：1, the face-centered cubic （fcc） Co3O4 powder shows the discharge capacity of 760.9 mA h g-1, the high coulombic efficiency of 99.7% in the first cycle at the current density of 125 mA g-l, and the excellent cycling performance with the reversible capacity of 442.3 mA h g-1 after 20 cycles at the current density of 250 mA g-1.
基金
supported by Project Supported by the Planned Science and Technology Project of Hunan Province, China(Nos.2011F J3160,2011GK2002)
Project Supported by Scientific Research Fund of Hunan Provincial Education Department(10B054)