摘要
Interdiffusion in the Fe203-TiO2 system was investigated by the diffusion couple method in the temperature range of 1323 to 1473 K. The diffusion concentration curves of Ti4＋ cations were obtained by electron probe microanalysis, according to which the Boltzmann-Matano method optimized by Broeder was used to calculate the interdiffusion coeffi- cients. The interdiffusion coefficients almost increased linearly with the mole fraction of Ti4＋ cations increasing, and they were in the range of 10-12-10-11cm2-s-1. The increase of temperature could also lead to the increase of the interdiffusion coefficients at a constant concentration of Ti4＋ cations. It was also found that the thickness growth of the diffusion layer obeyed the parabolic rate law.
Interdiffusion in the Fe203-TiO2 system was investigated by the diffusion couple method in the temperature range of 1323 to 1473 K. The diffusion concentration curves of Ti4＋ cations were obtained by electron probe microanalysis, according to which the Boltzmann-Matano method optimized by Broeder was used to calculate the interdiffusion coeffi- cients. The interdiffusion coefficients almost increased linearly with the mole fraction of Ti4＋ cations increasing, and they were in the range of 10-12-10-11cm2-s-1. The increase of temperature could also lead to the increase of the interdiffusion coefficients at a constant concentration of Ti4＋ cations. It was also found that the thickness growth of the diffusion layer obeyed the parabolic rate law.
基金
financially supported by the National Natural Science Foundation of China (No. 51090384)