In this work, the Pd-based catalysts were designed via immobilizing Pd nanoparticles on graphite oxide (GO) modified with organic base, 1,1,3,3-tetramethylguanidine (TMG), which was used for the selective hydrogenation of citral. These catalysts were characterized by various techniques including IR, X-ray diffraction, transmission electron microscopy, and X-ray photoelectron spectroscopy. It was demonstrated that the Pd particles with size less than 5 nm were uniformly distributed throughout the support, and they were in the electron-deficient state due to the strong interactions with the modified support. The resultant Pd-TMG/GO catalyst displayed high efficiency for the selective hydrogenation of citral with a turnover frequency of 7100 h-1 as well as superior selectivity to citronellal of 89.6%. Moreover, the catalyst can be reused for five times without obvious activity loss, which may result from its stable structure.
In this work, the Pd-based catalysts were designed via immobilizing Pd nanoparticles on graphite oxide （GO） modified with organic base, 1,1,3,3-tetramethylguanidine （TMG）, which was used for the selective hydrogenation of citral. These catalysts were characterized by various techniques including IR, X-ray diffraction, transmission electron microscopy, and X-ray photoelectron spectroscopy. It was demonstrated that the Pd particles with size less than 5 nm were uniformly distributed throughout the support, and they were in the electron-deficient state due to the strong interactions with the modified support. The resultant Pd-TMG/GO catalyst displayed high efficiency for the selective hydrogenation of citral with a turnover frequency of 7100 h-1 as well as superior selectivity to citronellal of 89.6%. Moreover, the catalyst can be reused for five times without obvious activity loss, which may result from its stable structure.
基金
financially supported by the National Natural Science Foundation of China (20903105, 21073202)
Chinese Academy of Sciences (KJXC2.YW.H30)