摘要
以铸造SiCp增强铝基复合材料为对偶,采用MM-1000摩擦磨损试验机研究了树脂基中酚醛树脂和丁腈橡胶3种不同配比对摩擦材料性能的影响。结果表明,基体酚醛树脂与丁腈橡胶的配比为6∶14、制动压力为0.36 MPa时,树脂基摩擦材料平均摩擦因数在0.3左右,制动压力为0.5 MPa时,平均摩擦因数在0.27左右,且摩擦扭矩曲线比较平稳,摩擦材料磨损量小,磨擦表面磨屑少,具有较好的耐磨性,其综合性能较好。
With cast SiCp reinforced aluminum matrix composites as the dual, the effects of three different ratio between phenolic resin and nitrile on the properties of resin based friction material had been investigated in this paper using MM-1000 friction and wear tester. The results showed that the resin-based friction material had better overall performance when the ratio of phenolic resin and nitrile rubber was 6 ： 14, the more stable curve of friction torque, fewer wear loss, fewer abrasive dust and better wear resistance, and when brake pressure was 0.36 MPa, the average friction coefficient was about 0.3, when brake pressure was 0.5 MPa, the average friction coefficient was about 0.27.
出处
《非金属矿》
CAS
CSCD
北大核心
2013年第1期77-80,共4页
Non-Metallic Mines
基金
国家自然科学基金(51102089)
湖南省自然科学基金(12JJ4046)
关键词
铝基复合材料
丁腈橡胶
酚醛树脂
摩擦磨损性能
aluminum matrix composites nitrile rubber phenolic resin friction and wear properties