摘要
研究了燃气轮机叶片用镍基高温合金在800℃、850℃和900℃下分别长期时效1 000 h、3 000 h和5 000 h后的组织。结果表明,γ'沉淀相生长动力学遵循LSW熟化理论,长期时效过程中一次碳化物MC主要退化为M23C6型碳化物,且未发现有害相TCP相,表明合金具有良好的热稳定性。
Microstructural evolution of a nicle-base directionally solidified superalloy during long-term thermal exposure at 800℃,850℃ and 900℃ for 1000 h,3000 h and 5000 h is investigated in this research.The results obtained from the growth kinetics of γ′ precipitates in this superalloy are presented.It has been found that the overall kinetic of coarsening follows a linear trend in this system,as predicted by Lifshitz,Slyozov and Wagner（LSW） theory.The carbide product of primary MC degeneration in this alloy is mainly M23C6.The TCP phases are not found during thermal exposure,which confirms this alloy has a good thermal stability.