A method to identify complex Young＇s modulus of viscoelastic materials using forced longitudinal vibration of slender rods is proposed. The method differs from the beam one. Experimental tests were carried out at room temperature with different lengths in 108 mm, 100 mm, 90 ram, 83.5 mm, 80 ram, 74.5 mm, 70 mm for the polycarbonate bars, and the curves of ratios A2/A1 between two ends of a viscoelastic bar versus frequencies are obtained, furthermore, the corresponding 3 dB bandwidth and the storage and loss modulus can be calculated. Sufficient number of obtained complex Young＇s modulus at different frequency allows us to calculate other ones using the least square method. If the step of the tested frequency is 5 Hz, the maximum error of results can be less than 6%. By comparison with the measurement methods which the previous literature mentioned, this new method simplifies the calculation, and the physical meaning appears apparently and clearly.
A method to identify complex Young＇s modulus of viscoelastic materials using forced longitudinal vibration of slender rods is proposed. The method differs from the beam one. Experimental tests were carried out at room temperature with different lengths in 108 mm, 100 mm, 90 ram, 83.5 mm, 80 ram, 74.5 mm, 70 mm for the polycarbonate bars, and the curves of ratios A2/A1 between two ends of a viscoelastic bar versus frequencies are obtained, furthermore, the corresponding 3 dB bandwidth and the storage and loss modulus can be calculated. Sufficient number of obtained complex Young＇s modulus at different frequency allows us to calculate other ones using the least square method. If the step of the tested frequency is 5 Hz, the maximum error of results can be less than 6%. By comparison with the measurement methods which the previous literature mentioned, this new method simplifies the calculation, and the physical meaning appears apparently and clearly.
基金
supported by the Fundamental Research Funds of China for the Central Universities(GK201001008)